 หัวเรื่อง:ไม่มีชื่อไทย (ชื่ออังกฤษ : Quality Improvement for Steel Wire Coating by the Hot-Dip Galvanizing Process to A Class Standard: A Case Study in a Steel Wire Coating Factory) ผู้เขียน: Pongthorn Ruksorn,  ดร.ประไพศรี สุทัศน์ ณ อยุธยา, รองศาสตราจารย์ สื่อสิ่งพิมพ์:pdf AbstractDemand for steel wire zinc coating by galvanizing to the A class standard is increasing because it protects the wire rod from corrosion. It can be applied to various types of products used in electrical equipment and construction. There are several factors and their levels in the hot-dip galvanizing process that affect the quality of A class galvanized steel wire such as the zinc bath temperature and withdrawal speed. If these factors and their levels are not properly controlled, the mass of zinc coating used will be more than the required standard (greater than 259 g.m-2). The objective of this research was to apply a 2k split-plot experiment to study the effects of factors on the hot-dip galvanizing process to the A class standard. The results showed that the interaction between the zinc bath temperature with each of the charcoal wiping condition, the free zinc length and the withdrawal speed, and the interaction between the charcoal wiping condition and each of the free zinc length and the withdrawal speed significantly affected the mass of zinc coating in the hot-dip galvanizing process to the A class standard. Thus, the appropriate settings were determined to reduce the mass of zinc coating. The confirmation results indicated that after applying the new settings, the mass of zinc coating conformed to the required standard. |
 |
|
|
|
|
ผลงานตีพิมพ์ในวารสารวิชาการCrystal Structure, Lattice Strain, Morphology and Electrical Properties of SnO2 Nanoparticles Induced by Low Calcination Temperatureผู้แต่ง:Dr.Panya Khaenamkaew, Associate Professor , Ms.Dhonluck Manop, Assistant Professor , Mr.chailoek thanghengjaroen, Lecturer , Mr.worasit Palkawong Na-Ayutaya, Assistant Professor , วารสาร:    
|
|
หัวเรื่อง:ไม่มีชื่อไทย (ชื่ออังกฤษ : Monitoring Insecticide Resistance Development in Beet Armyworm, Spodoptera exigua (H?bner) (Lepidoptera: Noctuidae)) ผู้เขียน:Md. Abdullah, Ouab Sarnthoy, ดร.ศิริพรรณ ตันตาคม, รองศาสตราจารย์ , Somchai Isichaikul, ดร.สุดาวรรณ เชยชมศรี สื่อสิ่งพิมพ์:pdf AbstractField collected larvae of beet armyworm, Spodoptera exigua (H?bner) were reared and evaluated for resistance against cypermethrin 10 EC, neem extract (Azadirachtin 0.1%) and Bacillus thuringiensis Berliner var. kurstaki (53,000 SU per mg) for 12 generations under laboratory condition by using leaf dip bioassay. Cypermethrin showed LC50 value of 251 ppm at F1 generation and decreased gradually to onward generations resulting LC50 value of 90 ppm at F12 generation for non-selection, whereas LC50 increased rapidly with a value of 8625 ppm at F12 generation under selection pressure. Neem extract exhibited LC50 value ranging from 3.98 ppm to 9.99 ppm for non-selection, whereas under selection pressure LC50 ranged from 4.38 ppm to 13.04 ppm throughout the generations. Bacillus thuringiensis var. kurstaki showed LC50 value which ranged from 7.3 ? 106 SU/L to 15.9 ? 106 SU/L for non-selection, and selection for resistance monitoring gave LC50 value ranged from 7.6 ? 106 SU/L to 73.9 ? 106 SU/L . Compared with non-selection strain, selection strain exhibited 95.83-fold, 1.44-fold and 5.6-fold increase in the LC50 for 12 generations against cypermethrin, neem extract and Bacillus thuringiensis var. kurstaki, respectively. |
ที่มา:Agricultural Science Journal (วารสารวิทยาศาสตร์เกษตร)หัวเรื่อง:ผลของอุณหภูมิการแช่ต่อการเกิดสีน้ำตาลในมะเขือเปราะตัดแต่งสด |
ที่มา:Agricultural Science Journal (วารสารวิทยาศาสตร์เกษตร)หัวเรื่อง:ผลของน้ำร้อนต่อจำนวนจุลินทรีย์ปนเปื้อนที่ก่อให้เกิดโรคกับมนุษย์ของตะไคร้ตัดแต่งสด |
ที่มา:IE Network 2004หัวเรื่อง:การออกแบบการทดลองเพื่อปรับปรุงประสิทธิภาพกระบวนการชุบผิวลวดเหล็กด้วยสังกะสีโดยวิธีการจุ่ม ที่ระดับ ค |