 หัวเรื่อง:ไม่มีชื่อไทย (ชื่ออังกฤษ : Development of an External Rubber-Clay Plaster Stabilized with Alkaline Sodium Silicate to Improve Adobe Wall Rain Resistance) ผู้เขียน: Pitiwat Wattanachai, Eakphisit Banjongkliang, Rattapoohm Parichatprecha สื่อสิ่งพิมพ์:pdf AbstractAn external clay plaster stabilized with blended prevulcanized rubber latex and sodium silicate was developed to enhance the poor water resistance of adobe walls. Sodium silicate was added to act as a pH stabilizer maintaining the pH and liquidity of the rubber latex during the manufacturing process. The study characterized the adobe plasters using an accelerated spray test, capillary absorption and microstructure investigation in terms of surface morphology, chemical analysis and porosity. The results showed that adding 3–5% sodium silicate could preserve the liquidity of 5–10% rubber latex during the mixing process. The newly developed sodium silicate + rubber-clay substrates had the highest water resistance in term of both rain resistance and water tightness, when compared with traditional clay plaster, rubber-clay plaster and stabilized rubber-clay plasters with a low sodium silicate content. The microstructure investigations confirmed that the alkaline-stabilized rubber latex could distribute throughout the substrate, was bound to most of the soil particles and filled capillary pores when dried. The stabilized-clay plaster with blended 10% rubber and 5% sodium silicate performed best, eroding only 1.2 cm after a spray test that approximated 50 yr of 1,800 mm annual rainfall, an above average annual amount for Thailand. |
 |
หัวเรื่อง:ไม่มีชื่อไทย (ชื่ออังกฤษ : Evaluation of Strength and Microstructure of Adobe Stabilized with Blended Rubber Latex and Sodium Silicate) ผู้เขียน:Eakphisit Banjongkliang, Pitiwat Wattanachai, Rattapoohm Parichatprecha สื่อสิ่งพิมพ์:pdf AbstractAdobe stabilized with blended, prevulcanized rubber latex and sodium silicate was developed to enhance the low strength of traditional adobe. Sodium silicate was investigated for its action as a pH stabilizer to maintain the pH and liquidity of rubber latex during the manufacturing process. The study characterized the adobe by its compressive strength, flexural strength and microstructure investigation in terms of surface morphology, chemical analysis, functional groups of molecules and porosity. The results showed that adding 3–5% sodium silicate could preserve the liquidity of 5–10% rubber latex during the mixing process. The study in the functional groups of molecules showed the possibility of sodium silicate as a secondary binder and rubber reinforcement. The investigation of the microstructure of stabilized adobe confirmed that alkaline-stabilized rubber latex could distribute throughout the substrate, bind most of the soil particles and fill the capillary pores when dried. The newly developed sodium-silicate-rubber-clay substrates had better strength when compared with traditional clay adobe, rubber-clay adobe and stabilized rubber-clay adobe with low sodium silicate content. The 3% sodium silicate-10% rubber stabilized adobe had the best performance with compressive strength (3.23 MPa or 237.19% of traditional clay adobe) and flexural strength (1.60 MPa or 298.91% of traditional clay adobe). |
|
|
ที่มา:การประชุมทางวิชาการของมหาวิทยาลัยเกษตรศาสตร์ ครั้งที่ 49หัวเรื่อง:การเพิ่มประสิทธิภาพบล็อกดินดิบด้านการรับแรงด้วยปูนขาวและขี้เถ้าปาล์มน้ำมัน |
ที่มา:ส่วนตัวหัวเรื่อง:การประเมินคุณลักษณะของเนื้อสุกรโดยวิธีการวิเคราะห์ภาพถ่ายดิจิตอลด้วยโปรแกรมคอมพิวเตอร์ |
 Researcherนาย พีรยุทธ นิลชื่นที่ทำงาน:ภาควิชาสัตวบาล คณะเกษตร สาขาที่สนใจ:ระบบสืบพันธุ์สัตว์, วิทยาศาสตร์น้ำนม, วิทยาศาสตร์เนื้อ, , การผลิตโคและกระบือ, สาขาเทคโนโลยีชีวภาพทางระบบสืบพันธุ์สัตว์ และสาขาการผลิตโคเนื้อและโคนม Resume |
 |
 |